Silica Brick
INDEX |
FR-1-S096 |
FR-2-S094 |
FR-3-S095 |
|
SIO2 |
≥96% |
≥94 |
≥95 |
|
FE2O3 |
0.8-1.0% |
1% |
1.30% |
|
AL2O3 |
≤1.0% |
≤1.0 |
≤1.0% |
|
TRUE DENSITY |
2.34G/CM3 |
2.34G/CM3 |
2.32G/CM3 |
|
COLD CRUSHING |
40MPA |
45MPA |
45MPA |
|
STRENGTH |
||||
APPARENT POROSITY |
23% |
22% |
23% |
|
REFRACTORINESS |
1710℃ |
1710℃ |
1710℃ |
|
REFRACTORINESS |
1650℃ |
1650℃ |
1650℃ |
|
UNDER LOAD 0.2 MPA |
||||
RLC (1450℃ X 2H) |
±0.2% |
±0.2% |
±0.2% |
|
RESIDUAL QUARTZ |
≤1% |
≤1% |
≤1% |
Light Weight Silica Brick | |
INDEX |
FR-1-LS091 |
SIO2 |
≥91 |
FE2O3 |
0.8-1.0 |
AL2O3 |
≤1.0 |
BULK DENSITY (G/CM3) |
1.00, 1.1, 1.15, 1.20 |
COLD CRUSHING |
|
STRENGTH (MPA) |
2.0, 3.0, 5.0, 5.0 |
REFRACTORINESS |
|
UNDER LOAD 0.2 MPA (℃) |
1400, 1420, 1500, 1520 |
TERMAL CONDUCTIVITY |
|
(350℃ CW/M.K) |
0.55, 0.60, 0.65, 0.70 |
Thank you >>